Creep of three-phase alloy Fe-30%Al-5.2%Zr
DOBES, F., KRATOCHVÍL, P., KEJZLAR, P.
vol. 53 (2015), no. 3, pp. 127 - 132
DOI: 10.4149/km_2015_3_127

Abstract
Compressive creep of alloy based on Fe-30at.%Al with addition of 5.2 at.% zirconium was studied at temperatures from 650 to 900 °C. The alloy was tested in two different states: (i) cast and (ii) annealed at 1000 °C for 50 h. The microstructure of cast alloy consisted of matrix (α/B2/D03) and fine lamellar eutectic composed of λ1 and (α/B2/D03). The eutectic decomposed during annealing at 1000 °C into λ1 and τ1 phases. Stress exponents and activation energies were estimated. The values of the stress exponent n can be explained by dislocation motion controlled by climb. The values of the activation energy in both cast and annealed alloy are greater than the activation enthalpy of diffusion. Creep exposure at 900 °C for about 50 h is probably sufficient for attainment the three-phase structure because the same microstructure was observed after creep at 900 °C, in both as-cast and annealed states. In contrast, creep expositions at 650 and 700 °C did not influence the appearance of microstructure.

Key words
iron aluminides, internal stresses, creep, precipitation

[open article.pdf] Full text (480 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.8.0      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2024-12-03 11:31      
Articles in press revised: 2024-12-05 09:43     
Full text pdf uploaded: 2024-12-03 11:34    
Information updated: 2023-04-19 16:14   
Code last revised: 2024-03-06 11:13  

© OldSoft, 2004, …, 2024