Deformation behavior of AZ61 magnesium alloy systematically rolled and annealed at 450 °C
vol. 54 (2016), no. 3, pp. 147 - 151

Magnesium alloy AZ61 was processed by several thermomechanical routes consisting of hot-rolling at a high strain rate •ε = 1.6 s–1 and intermediate annealing. The total reduction of thickness was 83 % after three routes. Intermediate annealing between routes was necessary to avoid sample fracture and to enhance the ductility. Texture investigations revealed that the basal type texture after deformation changed during a short time of annealing and the {11&1macr;0}<10&1macr;0> component was strengthened. The structure investigations after rolling show the occurrence of a large fraction of twins inside the grains while after annealing no twins were left. It was found that the twins formed during rolling may support the texture transformation during annealing and enhance the ductility.

Key words
texture, twinning, magnesium alloys, recrystallization,

[open article.pdf] Full text (465 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.7.2      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.

Article abstracts updated: 2021-05-11 12:09      
Articles in press revised: 2021-06-11 08:55     
Full text pdf uploaded: 2021-05-07 11:19    
Information updated: 2020-06-29 17:09   
Code last revised: 2020-06-29 16:48  

© OldSoft, 2004, …, 2021