The influence of the heat treatment on mechanical and microstructure properties of Fe-Mn-C high-manganese steel
AKINAY, Y., HAYAT, F.
vol. 54 (2016), no. 2, pp. 91 - 96

Abstract
The influence of the heat treatment on mechanical properties and microstructures of the Fe-22Mn-0.6C high-manganese steel was investigated at different annealing temperatures. A high-Mn TWIP (Twinning Induced Plasticity) steel specimens (0.6C, 24Mn steel) were fabricated, and were annealed at 700, 900 and 1100 °C for 150 min and then air-cooled. The carbide precipitates in the microstructure of specimens were annealed at 700 °C. However, the microstructure of specimens annealed at 900 and 1100 °C is austenite and some grains include annealing and mechanical twins. The results show that tensile strength of the material decreased, and the ductility of material was improved with increasing annealing temperature. Besides that, hardness value decreased between 700 and 1100 °C, which shows a good agreement with the equilibrium dissolution temperature of M3C carbides.

Key words
high-manganese steel, heat treatment, SEM, cold rolling, TWIP steel, microstructure

[open article.pdf] Full text (681 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.8.0      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2023-10-26 07:45      
Articles in press revised: 2024-03-26 11:42     
Full text pdf uploaded: 2023-11-08 06:53    
Information updated: 2023-04-19 16:14   
Code last revised: 2024-03-06 11:13  

© OldSoft, 2004, …, 2024