Microstructure characteristics of Ti-2Al-Mn/Al 1060 dissimilar joint by pulsed gas metal arc welding-brazing
WEI, S., LI, Y., WANG, J., LIU, K., ZHANG, P.
vol. 52 (2014), no. 5, pp. 305 - 311

Abstract
Butt welding-brazing of titanium alloy Ti-2Al-Mn to aluminum 1060 plates was investigated by pulsed gas metal arc welding using an AlSi5 filler wire. Microstructure characteristics of Ti/Al dissimilar joint were observed by scanning electron microscope. Chemical composition and phase constituent of Ti-Al transition region were investigated using energy-dispersive spectrometer and X-ray diffraction. Micro-hardness distribution of the weld zone was tested by micro-sclerometer. The experiment results indicated that joint free of pores and cracks could be obtained by controlling the welding process. The weld metal was composed of α-Al dendrites and α-Al+Si eutectic phase. The intermetallic compound TiAl3 appeared in the weld metal. A multilayered Ti-Al transition region containing TiAl3, Ti7Al5Si12 and α-Ti had formed adjacent to the Ti/Al interface. Micro-hardness of the transition region was about 280HV0.05. The heat-affected zone of Ti-2Al-Mn alloy was mainly composed of acicular α′ and lath α′ martensite phases. Micro-hardness of the heat-affected zone was 220–270HV0.05.

Key words
Ti-2Al-Mn alloy, Al 1060, pulsed gas metal arc welding, microstructure, micro-hardness

[open article.pdf] Full text (676 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.8.0      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2023-10-26 07:45      
Articles in press revised: 2024-03-26 11:42     
Full text pdf uploaded: 2023-11-08 06:53    
Information updated: 2023-04-19 16:14   
Code last revised: 2024-03-06 11:13  

© OldSoft, 2004, …, 2024